The thermoforming blank made of PETG (polyethylene terephthalate glycol) is supplied with an insulating film for the purpose of high transparency. Since it is tough-elastic and can be built up with acrylate, it is particularly suitable for Aligners, bite and occlusion splints, as well as orthodontic appliances.
Intended use: Dental thermoforming foil for the production of occlusal splints
Manufacturer: Dreve Dentamid GmbH
Colour: clear transparent
Foil thickness:
0.5 mm ± 0.1 mm
0.625 mm ± 0.1 mm
0.75 mm ± 0.1 mm
1.0 mm ± 0.1 mm
1.5 mm ± 0.15 mm
2.0 mm ± 0.2 mm
3.0 mm ± 0.3 mm
Diameter: Ø 120mm (special sizes according to demand)
Density: 1.27 g/cm3 ISO 1183-1
Elongation at break: > 35 % ISO 527-2/1B/50
E-module: 2020 MPa ISO 527-2/1B/1
Rockwell- hardness: R104 – 107 ASTM D785
Tensile strength: 45 MPa ISO 527-2/1B/50
Humidity absorption: 0.2 % 24 hrs. at 23 °C / 3 mm
Temperature area: -40 °C - +65 °C
Characteristics:
Biolon bonds with acrylate.